indexado en
- Base de datos de revistas académicas
- Abrir puerta J
- Genamics JournalSeek
- Claves Académicas
- DiarioTOCs
- Infraestructura Nacional de Conocimiento de China (CNKI)
- CiteFactor
- cimago
- Directorio de publicaciones periódicas de Ulrich
- Biblioteca de revistas electrónicas
- Búsqueda de referencia
- Universidad Hamdard
- EBSCO AZ
- OCLC-WorldCat
- Catálogo en línea SWB
- Biblioteca Virtual de Biología (vifabio)
- Publón
- miar
- Comisión de Becas Universitarias
- Fundación de Ginebra para la Educación e Investigación Médica
- pub europeo
- Google Académico
Enlaces útiles
Comparte esta página
Folleto de diario
Revistas de acceso abierto
- Administración de Empresas
- Agricultura y Acuicultura
- Alimentación y Nutrición
- Bioinformática y Biología de Sistemas
- Bioquímica
- Ciencia de los Materiales
- Ciencia general
- Ciencias Ambientales
- Ciencias Clínicas
- Ciencias farmacéuticas
- Ciencias Médicas
- Ciencias Veterinarias
- Enfermería y Cuidado de la Salud
- Genética y Biología Molecular
- Ingeniería
- Inmunología y Microbiología
- Neurociencia y Psicología
- Química
Abstracto
Preparation and Optimization of PEG-PLGA Loaded with Vincristine Sulfate and its In vitro Release
WEN Jia-Gen, GUO Tingting, ZHU Hong-Yuan, XIAO Yi-Yun, ZHANG Xiu-Zhen, CHEN Guo and CHEN Yuxiang
The aim of this study was to prepare the PEG-PLGA loaded with vincristine sulfate nanoparticles (VCR-loaded PEG-PLGA-NPs) and investigate its in vitro release properties. VCR-loaded PEG-PLGA-NPs were prepared by the modified double emulsion (W1/O/W2) method, and the main experimental factors influencing the characteristics of the nanoparticles were investigated and the preparation was optimized. The results showed that the physicochemical characteristics of VCR-loaded PEG-PLGA-NPs were affected by the polymer concentration, the ratio of internal water phase to oil phase, external water phase to oil phase and ultrasound time for the second time. VCR-loaded PEG-PLGA-NPs, with average particle size of 135.9nm, zeta potential of -12.83mV, encapsulation efficiency of 68.2% and drug loading of 8.34%, were prepared under optimal conditions. The release experiments in vitro showed the VCR release from PEG-PLGA-NPs exhibited consequently sustained release for more than 13d, which was in accordance with Higuchi equation.